Product Types and Properties |
|
 |
| Polyvinyl Chloride Resins / Sekisui PVC-HA |
 |
Heat Deflection Temperature
|
| *1 JIS K7207 Load: 0.45MPa |
| *2 JIS K7191 Load: 1.80MPa |
|
Basic Composition
|
Sekisui PVC-HA or PVC
|
100PHR |
| Tin stabilizers (Liquid) |
1.5PHR |
| Tin stabilizers (polymer) |
0.5PHR |
| High-grade fatty acid |
0.7PHR |
| Ester wax |
2.3PHR |
| MBS |
10PHR |
|
Test specimen molding conditions
PVC-HA and PVC |
| Roll: |
Temperature |
200°C |
| |
Milling Time |
3min. after wrap |
| Press |
Temperature |
200°C |
| |
Milling Time |
5min. pre-heat |
| |
|
5min. pressure |
| |
Molding pressure |
7.5MPa |
|
|
|
| Polyvinyl Chloride Resins / Sekisui Compound |
Applications
•Automobile parts: Weather strips, garnishes, roof moldings, parts in the car.
•Building material parts: Bathroom doors and panels, and window frames.
•Electrical parts: Trunk air outlet panels, wiring ducts, and switch boxes.
•Corrosion resistant factory parts: Pipes, joints, valves, channels, and filler.
•Industrial equipment, air conditioner parts: Spiral ducts, pump casings, and gear wheels.
•Other: IC cases, thread nozzle holders, and engineering plastic dies.
|
| Applications |
| Grade Name |
Heat Deflection
Temperature *1 |
Specific
Gravity |
Tensile
Strength |
Elongation
Ratio |
| C |
- |
MPa |
% |
| |
|
JIS
K7191 |
JIS
K7112 |
JIS
K7113 |
JIS
K7113 |
| High-Heat Resistance Extrusion Grade |
| EH-152F 80°C |
|
80 |
1.50 |
46 |
100 |
EH-153F 80°C
|
High weather
resistance |
80 |
1.50 |
46 |
100 |
EH-250F 85°C
|
|
85 |
1.49 |
51 |
80 |
EH-350F 90°C
|
|
90 |
1.50 |
49 |
70 |
EH-351F 90°C
|
High weather
resistance |
90 |
1.47 |
51 |
120 |
EH-355F 90°C
|
|
90 |
1.50 |
49 |
70 |
EH-452H 95°C
|
|
95 |
1.51 |
49 |
50 |
EH-455H 95°C
|
|
95 |
1.48 |
49 |
50 |
EH-459KG 95°C
|
|
95 |
1.52 |
58 |
60 |
EH-550K 100°C
|
|
100 |
1.54 |
51 |
80 |
Normal vinyl
chloride 70°C |
|
70 |
1.47 |
47 |
150 |
| High-Heat Resistance Injection Grade / Extrusion Grade |
| SH-215F |
|
82 |
1.45 |
53 |
90 |
| SH-415K |
|
93 |
1.46 |
53 |
50 |
| SH-426KG |
|
90 |
1.50 |
53 |
40 |
| High Impact Grade |
| G-320T |
|
- |
1.34 |
44 |
200 |
| G-520T |
|
- |
1.30 |
34 |
140 |
| Wood Foaming Grade |
| F-102T |
|
- |
1.50 |
35 |
40 |
|
| Grade Name |
Charpy impact Strength |
Izod Impact
23°C |
Flexural
Strength |
Flexural
Modulus |
| 23°C |
0°C |
-20°C |
| kJ/m2 |
kJ/m2 |
kJ/m2 |
kJ/m2 |
MPa |
MPa |
| |
|
JIS
K7111 |
JIS
K7111 |
JIS
K7111 |
JIS
K7110 |
JIS
K7171 |
JIS
K7171 |
| High-Heat Resistance Extrusion Grade |
| EH-152F 80°C |
|
13 |
- |
- |
11 |
69 |
2,850 |
EH-153F 80°C
|
High weather
resistance |
12 |
- |
- |
11 |
68 |
2,790 |
EH-250F 85°C
|
|
14 |
- |
- |
14 |
74 |
2,620 |
EH-350F 90°C
|
|
14 |
- |
- |
12 |
75 |
2,750 |
EH-351F 90°C
|
High weather
resistance |
18 |
- |
- |
20 |
74 |
2,650 |
EH-355F 90°C
|
|
16 |
- |
- |
15 |
73 |
2,700 |
EH-452H 95°C
|
|
20 |
- |
- |
22 |
71 |
2,600 |
EH-455H 95°C
|
|
20 |
- |
- |
22 |
69 |
2,600 |
EH-459KG 95°C
|
|
27 |
|
|
|
85 |
2,500 |
EH-550K 100°C
|
|
11 |
- |
- |
10 |
71 |
2,610 |
Normal vinyl
chloride 70°C |
|
20 |
- |
- |
22 |
64 |
2,450 |
| High-Heat Resistance Injection Grade / Extrusion Grade |
| SH-215F |
|
12 |
- |
- |
12 |
78 |
2,550 |
| SH-415K |
|
15 |
- |
- |
15 |
79 |
2,500 |
| SH-426KG |
|
11 |
- |
- |
11 |
90 |
2,650 |
| High Impact Grade |
| G-320T |
|
118 *2 |
39 |
|
- |
66 |
2,350 |
| G-520T |
|
128 *2 |
115 *2 |
98 *2 |
- |
49 |
1,960 |
| Wood Foaming Grade |
| F-102T |
|
4 |
|
- |
- |
67 |
3,800 |
|
All values are really measured, not guaranteed.
Heat Deflection Temperature
|
| *1 measured by 1.80Mpa without Anneal |
| |
| Charpy Impact Strength |
| *2 not broken |
|
Test specimen molding conditions
|
| Roll: |
Temperature |
190°C |
| |
Milling Time |
3min. after wrapping |
| Press |
Temperature |
190°C |
| |
Milling Time |
5min. pre-heat |
| |
|
5min. pressure |
| |
Molding pressure |
7.5MPa |
|
|
|
| |
Please contact us for details, using inqire form |
|